A mechanistic model to predict matte temperatures during the smelting of UG2-rich blends of platinum group metal concentrates
Date
2011
Authors
Eksteen J.J.
Journal Title
Journal ISSN
Volume Title
Publisher
Abstract
High matte temperatures can be related to numerous catastrophic furnace failures in the platinum group metal (PGM) industry where chromite-rich upper group 2 (UG2) concentrates are smelted. Chromite rich concentrates require high slag temperatures as well as sufficient mixing to suspend the chromite spinel particles in the slag and prevent settling in a so-called "mushy" layer consisting of a three phase emulsion of slag, matte and chromite particles. To achieve sufficient bath mixing and to melt and suspend chromite spinel build-up, high hearth power densities are utilised. However, high hearth power densities in conjunction with a heat-isolating concentrate layer, leads to high side wall heat fluxes which motivated the use of intensive cooling in the furnace side wall so that a slag freeze lining can be formed. If matte temperatures are above the slag liquidus temperature, any matte that comes into contact with the freeze lining can destroy the freeze lining. Moreover, if the matte temperature exceeds ca. 1500 °C, chemical thermodynamics indicate that matte has the ability to sulfidise MgO-FexO-Cr2O 3 refractories, leading to rapid wear of refractories exposed to high temperature flowing matte. Models are derived for the concentrate-to-matte and slag-to-matte droplet heat transfer. Calculations using the derived models, physical properties and furnace operating conditions give realistic matte temperatures and show that matte temperatures rapidly increase as the concentrate bed becomes matte drainage rate limiting. It is shown that for each concentrate blend mean particle size and mineralogy, there is a maximum smelting rate above which the concentrate bed becomes rate limiting with regards matte drainage, thereby significantly contributing to matte preheating, prior to further heat absorption from the slag layer. © 2010 Elsevier Ltd. All rights reserved.
Description
Keywords
Citation
Minerals Engineering
24
7
676
687
24
7
676
687