Masters Degrees (Civil Engineering)
Permanent URI for this collection
Browse
Browsing Masters Degrees (Civil Engineering) by Author "Badenhorst, Adriaan Jakobus"
Now showing 1 - 1 of 1
Results Per Page
Sort Options
- ItemDebonding of external CFRP plates from RC structures caused by cyclic loading effects(Stellenbosch : Stellenbosch University, 2012-03) Badenhorst, Adriaan Jakobus; Van Zijl, G. P. A. G.; Stellenbosch University. Faculty of Engineering. Dept. of Civil Engineering.ENGLISH ABSTRACT: This study set out to determine the debonding of externally applied Carbon Fibre Reinforced Polymer (CFRP) plates from RC structures under cyclic loading. Triplet shear tests and finite element (FE) analyses were done on the epoxy to determine the bond stress between the CFRP plate and a reinforced concrete specimen. From these tests and analyses the average shear strength of the bond between the epoxy and concrete substrate was determined and the shear strength of the epoxy specified by the supplier could be confirmed. A case study of a statically loaded beam was performed to verify the bond strength. Finally a reinforced concrete (RC) T-section was designed and pre-cracked to simulate a damaged beam in practice. These sections were then externally reinforced by bonding CFRP plates onto the face of the web. The sections were subjected to static and cyclic loading at different force amplitudes. Along with the experimental tests, FE models were developed and analysed which had the same geometrical and material properties as the experimental specimens. Due to time constraint a FE mesh objectivity study was not done, but the chosen element size is believed to be sufficiently small to replicate the experimental tests objectively. The FE analyses and the experimental tests yielded results that were close to each other on both the global scale and in terms of localised behaviour, thus it was decided that the computational approach could be used for the final design of a model of the debonding of CFRP plates bonded onto RC beams under cyclic loading because the data can be analysed more easily and a large variation of tests can be done. For the T-section 3 tests were conducted; a pull-off (static) test where the bonded CFRP plate was pulled from a specimen to get the ultimate failure envelope of the test specimens. The static test was followed by cyclic tests with force amplitude of 85% and 65% of the ultimate pull-off strength. Different measurements were taken to get the global and local displacement behaviour of the section. The global displacement was measured by means of a linear variable displacement transducer (LVDT, displacement meter) clamped onto the CFRP plate that pushed on the top of the concrete and the local displacement was measured with the help of the Aramis system. The displacement was then compared to the same displacements of nodes and elements in the FE models. The result was a confirmation that the results from the FE models were sufficient to design a model for cyclic debonding of CFRP plates from RC structures. From the FE models the relative displacement between the CFRP plate and concrete was obtained in the vicinity of a crack. This relative displacement was then normalised by the respective stress range of the different tests, from which the normalised relative displacement was plotted against the number of cycles to get an equation limiting the number of cycles for a specific stress range. From the results, it appears that for cyclic load levels up to 65% of the peak static resistance, a threshold number of load cycles are required for delamination initiation. Subsequently, a near constant delamination rate is reached. The delamination rate is significantly lower for lower cyclic load levels. Finally, an unstable delamination stage is reached at a level of about 65 μm for all the analyses, after which CFRP pull-off is imminent. Service life design of CFRP reinforcement of RC beams should take into consideration the delamination initiation threshold, the subsequent delamination rate and finally the initiation of unstable delamination.